Steel name

Steel number

C

Si

Mn

P

S

N b

S235JRH

1.0039

FF

0,17

—

1,40

0,040

0,040

0.009

S275J0H

1.0149

FF

0,20

—

1,50

0,035

0,035

0,009

S275J2H

1.0138

FF

0,20

—

1,50

0,030

0,030

—

S355J0H

1.0547

FF

0,22

0,55

1,60

0,035

0,035

0,009

S355J2H

1.0576

FF

0,22

0,55

1,60

0,030

0,030

—

S355K2H

1.0512

FF

0,22

0,55

1,60

0,030

0,030

—

a. The deoxidation method is designated as follows:

FF: Fully killed steel containing nitrogen binding elements in amounts sufficient to bind available nitrogen (e.g. min. 0,020 % total Al or 0,015 % soluble Al).

b. The maximum value for nitrogen does not apply if the chemical composition shows a minimum total Al content of 0,020 % with a minimum Al/N ratio of 2:1, or if sufficient other N-binding elements are present. The N-binding elements shall be recorded in the Inspection Document.

Steel 

name

Steel number

Specified thickness

mm

Specified thickness mm

Specified thickness mm

at test temperature of

£ 16

> 16 £ 40

< 3

³ 3 £ 40

£ 40

-20°C

0 °C

20 °C

S235JRH a

1.0039

235

225

360-510

360-510

24 b

-

-

27

S275J0H a

1.0149

275

265

430-580

410-560

20 c

-

27

-

S275J2H

1.0138

27

-

-

S355J0H a

1.0547

355

345

510-680

470-630

20 c

-

27

-

S355J2H

1.0576

27

-

-

S355K2H

1.0512

40 f

-

-

a. The impact  properties are verified only when Option 1.3 is specified.

b. For thicknesses > 3 mm and section sizes D/T < 15 (round) and (B+H)/2T < 12,5 (square and rectangular) the minimum elongation is reduced by 2. For thicknesses £ 3 mm the minimum value for elongation is 17 %.

c. For section sizes D/T<15 (circular) and (B+H)/2T<12,5 (square and rectangular) the minimum elongation is reduced by 2.

d. For thicknesses < 3 mm see   9.2.2.

e. For impact properties   for reduced section   test pieces see 6.7.2.

f. This value corresponds to 27J at –30 °C (see EN 1993-1-1).