Two Part Water Based Epoxy Resin Floor Emulsion Coating Paint

Min.Order : 1 Pieces Quick Quotation >

Conpany Profile

6 YRS Xiamen Wangqin Chemical Technology Co.,Ltd

Transaction Level:

Elizabethguo@xmcontinent.com

+8615359457600

Product Details

Find high quality two part water based epoxy resin floor emulsion coating paint with competitive price here. Please rest assured to buy two part water based epoxy resin floor emulsion coating paint with Xiamen Wangqin Chemical Technology Co.,Ltd

Two Part Water Based Epoxy Resin floor Emulsion Coating Paint WQ-EP503

EP503 epoxy resin features:

? Nonionic self-emulsifying epoxy

? Small particle size of emulsion

? Good film-forming properties

? Low VOC

EG043 curing agent features:

? Phenol modified aliphatic amine

? Good hydrophobic property

? Good compatibility

? Good resistance to media

EP503+EG043 features:

Film thickness: 50-60um at 80? for 30 mins, salt fog resistance: over 800 hours

Technical index of product:

Composition:epoxy resin,cosolvent,water

Appearance:milky white uniform liquid

Non-volatile matters(%):50±2

Viscosity(m Pa.s):=2000

PH value:4.0~8.0

Epoxy value(to solid):0.18~0.22

Product characteristics:

(1) The product contains no heavy metal and meets Rohs requirements;

(2) Excellent anti-rust and anti-corrosivity;

(3) Excellent water resistance and salt fog resistance;

(4) Good applicability

Applications:

As a water based epoxy emulsion, this product can prepare water based epoxy flooring coating, the paint for railway, locomotive, bridge and container, water based epoxy anti-corrosive paint, household paint and metal paint.

Storage:

This product should be stored in sealed containers at a cool place at 5-40?, with the shelf life of 6 months. The expired products can be used after passing the test.

WQ-EP503 Test Form

Primer Test Result

Item		Test Result	Test Method
Physical and Chemical Properties	Original paint	Uniform liquid	Visual check
	Paint film color	Light grey	Visual check
	Hiding power, g/m2	80	GB/T 1720-1979
	Original paint viscosity (T-4 cup at 25o) S	132s	GB/T 1723-1993
	Fineness, micron	=30	GB/T1724-1979
	Non-volatile matters, %	52	GB/T1725-2007
	Surface drying time, min at 23?	20	GB 1728-1979
	Hard drying time, h at 25?	5	GB 1728-1979
	Baking time, min at 65?	30	GB/T1728-1979
	Pot life, h at 25?	3	HG/T3668-2000-5.9
Mechanical Properties	Hardness (pencil)	H	GB/T 6739-2006
	Flexibility, mm	1	GB/T 1731-1993
	Impact resistance, KgNaN/50cm	pass	GB/T 1732-1993
	Grinability (20 times,320# sand paper	grindable	GB/T1770-2008
	Adhesion (Cross-cut tape test)	1	GB/T9286-1998
	Adhesion (circle-cut tape test)	1	GB/ 1720-1979
	Matching	Compatibility with other coating	Good
Corrosion resistance	Water resistance at 23?	240 h , no bubbling, peeling off and rusting	GB/T 1733-1993
	Alkaline resistance (at 25?, 0.1N NaOH)	48 h	GB/T9274-1998
	Acid resistance (at 25?, 0.1N H2SO4)	48 h, no bubbling	GB/T9274-1998
	Oil resistance (at 25?,10# Transformer oil)	48 h, no change	HGT/ 9274-1998
	Temperature alternating resistance (at -40? +60?)
	Salt fog resistance (480h)	Bubbling at cross, not bigger than 2 mm at a single side	GB 1771-2007

????.jpg

Other Product:

product name	non- volatile	epoxy equivalent	PH	viscosity (mPa.s)	specific gravity	properties	application
WQ-LP603	50±2	1000±50	6-8	200-900	1.10±0.01	small particle size uniform coating,good mechnical stability,can grind	two-component epoxy antirust paint
WQ-LP604	50±2	1000±50	6-8	200-900	1.10±0.01	good adhesion and salt fog-spray resistance	two-component epoxy antirust paint
WQ-LG040	40±2	350±30	8-10	3000-7000	1.06±0.01	quick crosslinking speed, excellent salt fog-spray resistance	used with epoxy emulsion,two-component epoxy antirust paint
WQ-LG043	43±2	350±30	8-10	3000-7000	1.06±0.01	long construction time limit,good salt fog-spray resistance	used with epoxy emulsion,two-component epoxy antirust paint